Addition silicone rubber for love dolls application:
*Rapid prototyping(urethane casting/silicone tooling/vacuum casting)
*GRC and Concrete molding
*PU resin casting
*General Mold making
*Superior manual mold design
*food grade molding application
molding process of addition silicone rubber for love dolls :
1.Mixing component A with B evenly according its mix ratio, it is ready for use after degassing,
it cures by heating up the temperature when pouring into the mold.
2.The curing time is subject to the temperature, short time will be required under high temperature,
long time will be required while the product with large thickness.
Characteristics:
-almost nil shrinkage
-high chemical resistance
- good tear strength
-high degree of precision in rereproducyion
-high dimensional stability over time and ageing(resist to -60 to 200)
-excellent non-stick effect
-food grade molding application
Notice :
Different typesof catalyst is available according to customer's specific requirements/
packaging :
Mold Making silicone Base is available in 5 kg,25kg and 200kg containers.
Curing Angent is available in 0.25 kg,1kg and 25kg containers.
addition silicone rubber for love dolls Data:
Model |
E615 |
E620 |
E625 |
Appearance |
Translucent |
Translucent |
Translucent |
Mixing Ratio |
1: 1 |
1: 1 |
1: 1 |
OperateTime(Mins25° C) |
2~3 |
2~3 |
2~3 |
CuringTime (Mins 25° C) |
30 |
30 |
30 |
Hardness (A° ) |
15± 2 |
20± 2 |
25± 2 |
Density ( g/cm 3 ) |
1.08 |
1.08 |
1.08 |
Viscosity (CS) (Part A) |
10000 ± 2000 |
20000 ± 2000 |
22000 ± 2000 |
Viscosity(CS)(Part B) |
5000 ± 500 |
5000 ± 500 |
4000 ± 500 |
Viscosity (CS) (After mixed) |
12000 ± 2000 |
12000 ± 2000 |
10000 ± 2000 |
Tensile-strength( kgf /cm 2 ) |
35± 5 |
46± 5 |
44± 5 |
Tear-strength (kgf /cm ) |
10± 2 |
11± 2 |
12± 2 |
Elongation-break(%) |
430 ± 50 |
460 ± 50 |
490 ± 50 |
Retractility(%) |
≤ 0.1 |
≤ 0.1 |
≤ 0.1 |
If you need more information about the silicone rubber or you want the sample to test, pls feel free to contact Herry: